Metal compounds with Vulkollan

The most diverse and very individual design possibilities are possible with Vulkollan® coated components.

Joints between Vulkollan® and metal can be easily produced after pretreatment of the metal component. During this pre-treatment, the surface of the component is cleaned and degreased using a sandblasting process. Subsequently, the application of an adhesion promoter guarantees an optimum bond.
The metal component (e.g. steel, aluminium, cast iron) assumes the function of a stable supporting body.

The Vulkollan® coating meets the highest performance requirements in terms of wear protection, damping and noise reduction.

Product features

The material Vulkollan® is characterized by outstanding properties that make it interesting for a variety of applications:

  • Award-winning mechanical wear resistance
  • High impact elasticity, even with hard settings
  • High tear propagation resistance
  • Low compression set
  • Good resistance to mineral oils, greases, petrol and various solvents

Applications

Metal compounds with Vulkollan® are used in many areas of industry where high performance requirements are placed on the coating:

  • Coatings for Wheels, Rollers and Rollers
  • Balls with solid or hollow metal cores
  • Coatings of valve seats
  • linings, skirting boards and throwing shovels with fixing reinforcements
  • Pipe cleaning pigs with steel or magnetic cores
  • Suction cup, gripper and sealing frame with metal adapter

Technical data

Properties
property
propriété
Propiedad
Test procedure
Test specification
spécification
Standard de control
Unit of measure
units
unité
Unidad de Medida
Types of Vulkollan®
18/40 18 21 25 30 40 60
Shore Hardness A/D
Shore hardness A/D
Dureté Shore A/D
DurezaShore A/D
DIN 53505 68 83/29 89/35 92/36 94/41 94/44 96/57
Stress at 100% elongation
Stress at 100% strain
Modules à 100% d´allongement
Tensión para un alargarniento del 100%
DIN 53504 MPa 2,5 4,3 5,9 8,0 10,6 11,28 19,9
Stress at 300% elongation
Stress at 300% strain
Modules à 300% d´allongement
Tensión para un alargamiento del 300%
DIN 53504 MPa 4,0 7,8 10,4 12,8 15,8 20,7 33,07
Tear Strength
Tensile strenth
Tension de rupture
Tensión de rotura
DIN 53504 MPa 35 44 43 41 35 44,58 32,21
Stretch at Break
Elongation at break
Allonment à la rupture
Alargamiento a la rotura
DIN 53504 % 600 663 696 741 702 433 293
Graves resistance
Taer propagation resistance
Resistance to the amorphous decision
Resistencia al desgarro progresivo
DIN 53515 kN/m 18 25 31 48 57 approx 60 approx 80
rebound elasticity
rebound resilience
rebondissement elastometry
Elasticidad de chogue
DIN 53512 % 45 65 64 62 61 --- ---
Abrasion
Abrasion resistance
Perte à l`abrasion
Perdida por abrasión
DIN 53516 mm2 40 37 32 28 26 27 25
Compression set
Compression set
Rémanenté Déformation à la compression
Deformación remanente por compresión
DIN 53517 % 10
15
12
20
12
20
12
20
13
21
12,5
24
16,2
27,7